High Quality Stearic Acid Amide Emulsion

Stearic Acid Amide Emulsion:
Stearic acidamide amide, a white emulsion is safe and healthy. The product can be easily dispersed in water, has low viscosity and is highly dispersible.
Stearamide may also be known as stearamide. Its chemical composition is C17H35CONH2. Stearic acidamide is insoluble when mixed with water. It can be slightly soluble at room temperature in organic solvents. This compound can enhance the dispersion of pigments and their affinity.
Excellent adhesion and lubricity. No moisture absorption. You can mix it with paraffin wax. Ammonium salt is created by the reaction between stearic and ammonia. It then gets dehydrated to get the final product. It is a good, smooth product that has low hygroscopicity. Use it as a pigment ink mixed agent, surface-active and fiber oil agent.
The use of stearamide in thermal paper coatings can serve as both a sensor and slip agent, and as an anti-blocking and slip agent for polyolefin films. The base of stearates is fatty saturated linear monocarboxylic oils derived from natural vegetable oil. Send an inquiry for the most current price to purchase bulk Stearic Acid Amide Emulsion.

Technical Information of Stearic Acid Amide Emulsion:

How does Stearic Acid Amide Emulsion get made?
Insoluble in water, stearic Acid amide must be prepared using emulsifiers. Even after adding dispersant, water-based stearic Acid amide emulsion is still not able to disperse well. Additionally, it can easily precipitate. Long-term storage may result in flocculation. Additionally, high-speed stirring is required and the grinding must be done under heat. The production costs are high.

First, add the water-based water-basedstearic Acid amide to water. Next stir for 60 minutes at 2500r/min. Then add defoamer (stirring frequency is 2500r/min), and then stir for 40 minutes at 2500r/min. To obtain the aqueous solution of stearic Acid amide. This prepared water-based, stearic-acid amide-amide emulsion contains 41.7% solids. It has a viscosity level of 146 mPa*S. After 30 minutes of centrifugation at 20000r/min, the defoamer and preservative were added to the mixture. Stearic-based stearic-acid amide-amide emulsion was kept at 20-35°C for three months with no flocculation or delamination

Stearic Acid Amide Emulsion:
Stearamide can be used to lubricate and release molds for polyvinylchloride, polystyrene, and other plastics.
As an antiblocking agent to polyolefin film films, stearamide should be combined with oleamide-erucamide.
Stearamide, unlike the common inorganic antiblocking agents (silica), does not affect the transparency. Stearamide is used to release synthetic rubber, natural rubber, and as a lubricant for rubber compounds. This gives the product a high Gloss.
The sensitizer of thermal paper is made from stearic Acid amide Ultrafine Aqueous Dispersion.
The ultra-fine, water-based, stearic Acid amide dispersion serves as textile waterproofing, fabric softener and antistatic agent. It also acts as a wetting agent.